ATC300 Material Composition

ATCORP , ATC-300 Bimetal bearing material structure have steel backing and sliding layer of CuPb10Sn10 with indent filled with graphite material.Steel Backing provide strength to Bimetal structure while Sliding layer of bronze along with Graphite provide self-lubricating properties.ATC-300 Material comes with three options like tin flash , copper flash or Zn Flashing also to avoid rusting of steel during transit /storage

ATC100
Performance IndexUnitsOil LubricatedGrease Lubricated
Max Dynamic LoadMpa140140
Max Staic LoadMpa140140
Working Temperature°C- 40 - + 250-140 - +150
Max Linear Velocitym/s52.5
Max Pv Valuesm/s x Mpa102.8
Min Alloy Layer HardnessHB6060
Coefficient of friction0.08 – 0.120.08 – 0.18

Benefits of ATC300

  • Due to graphite filled works as self-lubricated bearings.
  • Have negligible stick up.
  • Very good under vibratory and impact loading, very good wear resistance properties.
  • Can be machined to achieve tighter tolerances.
  • Can work for a long time without oil in the condition of boundary lubrication, under oil or grease lubrication interval, the working-life will be longer. Suitable for linear, swing, and rotary motion.
  • Dimensional stability due to heavy load carrying capacity under wide temperature range.
  • Seizure resistant.
  • Works well in grease lubricated condition, in Oil lubricated condition provide satisfactory result, however not recommended for dry applications.
  • High static and dynamic load capability.